ANYCUBIC ABS-Like Resin 3.0 (black)
ANYCUBIC ABS-Like Resin 3.0 is a photopolymer resin designed for LCD and DLP 3D printers, combining high mechanical strength, crack resistance, and high print accuracy. With an elongation at break of 25–30%, an impact strength of 130 J/m, and a low volumetric shrinkage rate (3.9–4.9%), it allows you to create durable models with a smooth surface and a very high level of detail. Low viscosity and minimal odor further enhance working comfort.
Greater flexibility and improved strength
ABS-Like Resin 3.0 is ideal for creating parts subjected to stress. With a hardness of 83–86 HD and high impact resistance, the finished models retain their durability even during drilling and further machining. The material also stands out for its very low susceptibility to warping, making it ideal for printing mechanical parts, device enclosures, and automotive components. Additionally, ABS-Like Resin 3.0 offers an elongation at break of up to 30%, which is nearly twice that of many standard ABS-type resins. These properties allow the material to better withstand stress and increase the models’ resistance to damage caused by everyday use.
High precision and shorter print times
Low shrinkage and an optimally selected viscosity of 280–300 mPa·s result in highly accurate detail reproduction and a smooth surface texture. The material’s good flow accelerates its return to the build volume, which helps reduce print time and increase productivity.
Comfort during printing and broad compatibility
The resin formula was developed to minimize odor and reduce the risk of irritation during use. You also don’t have to worry about compatibility issues—ABS-Like Resin 3.0 works with a wide range of LCD and DLP 3D printers that use UV light with a wavelength between 365 and 405 nm. This makes it ideal for both home workshops and more advanced projects.
| Manufacturer | ANYCUBIC |
|---|---|
| Model | ABS-Like 3.0 |
| Color | Black |
| Material | Photopolymer resin |
| Wavelength | 365–405 nm |
| Viscosity | 280–300 mPa·s (25°C) |
| Density | 1.06–1.09 g/cm³ |
| Hardness | 83–86 HD |
| Tensile strength | 38–45 MPa |
| Elongation at break | 25–30% |
| Flexural modulus | 50–65 MPa |
| Flexural strength | 1500–2000 MPa |
| Young’s modulus | 1300–1700 MPa |
| Izod impact strength | 130 J/m |
| Volumetric shrinkage | 3.9–4.9% |
| Printing temperature | 20–50°C |
| Recommended ambient temperature during printing | 20–40°C |
| Exposure time for the first layer | 23–40 s |
| Exposure time for a standard layer | 2–3.6 s |
| Cleaning agent | 95% IPA |
| Washing time | ≥3 min |
| UV wavelength during curing | 405 nm |
| Curing temperature | 18–30°C |
| UV irradiance | 25,000–30,000 µW/cm² |
| Curing time | 3 min |
| Weight | 1 kg |